Low-Carbon Steel for Cold Deformation and Carburizing

Low carbon steel with a chemical composition specially designed for cold deformation. The pieces obtained are generally subjected to carburization and tempering.

References and Comparable Standards

Standard Reference: EN 10263-2: 2017

EUROPE		ITALY	GERMANY		FRANCE	UK	USA
EN 10263-2: 2001		(UNI 7356 - 74)	(DIN 1654-2:89)		(NFA35-564:83)	-	ASTM
Grade	N°		Werkstoff	N°
(C10C)	(1.0214)	CB10FF	QSt36-3	1.0214	XC10FF	-	-

Chemical Composition (Cast Analysis) (%)

C	Si/max	Mn	P/max	S/max	Al
0,08÷0,12	0,10	0,30÷0,50	0,025	0,025	0,020÷0,060

Mechanical Properties

Size (mm)	Untreadted (+U) or Untreadted + Peeled (+U +PE)		Spheroidized (+AC) or as Treated + Peeled (+AC +PE)		Cold Drawn (+U +C)		Cold Drawn + Spheroidized + Skin Passed (+U +C +AC + LC)		Spheroidized + Cold Drawn (+AC +C)
Size (mm)	Rm (MPa) max	Z (%) min	Rm (MPa) max	Z (%) min	Rm (MPa) max	Z (%) min	Rm (MPa) max	Z (%) min	Rm (MPa) max	Z (%) min
2≤d≤5	-	-	-	-	-	-	410	68	-	-
5<d≤10	430	60	380	70	520	58	400	68	470	63
10<d≤40	430	60	380	70	510	58	400	68	460	63
40<d≤100	430	60	380	70	-	-	-	-	-	-

Working Temperatures Recommended

Operation	°C
Hot forgings deformation	850÷1100
Soft annealing	650÷700

Published: 01 January 2025 | Last Updated: 08 June 2026

C4C - Nr.1.0303

SB4

C10E - Nr.1.1121 C10R - Nr.1.1207

KV10 R10S R10Pb

C15E - Nr.1.1141

KV15 R15Pb

C16E - Nr.1.1148 C16R - Nr.1.1208

C16E